ABSTRACT
OBJECTIVE@#To study the effect of nanohydroxyapatite (nHA) for promoting surface mineralization of demineralized dentin discs and adsorption of lead ions in simulated sewage water.@*METHODS@#Sixty dentin disks were prepared from freshly extracted teeth with intact crown (including 30 premolars and 30 molars) and treated with 10% citric acid for 2 min to simulate dentinal tubules with dentin hypersensitivity. The etched dentin discs were brushed with distilled water, 0.2 g HA or 0.2 g nHA for 2 min twice a day for 7 consecutive days, after which scanning electron microscopy (SEM) was performed and calcium and phosphorus contents in the dentin discs were detected using EDS. Lead ion adsorption capacities of HA and nHA were tested by mixing 1 mL serial concentrations of HA and nHA suspensions with 50 mL lead ion solutions (1.0 mg/L). After 24 h, the residual lead ion concentration in the supernatant was measured using ICP to calculate lead ion adsorption rate and adsorption capacity of the materials.@*RESULTS@#SEM showed a smooth surface and empty dentin tubules in the acid- etched dentin dics. The dentin dics treated with HA were covered with masses of particles that loosely attached to the surface, and the diameter of the dentin tubules was reduced. In nHA group, the dentin discs showed a fine and homogeneous surface clogging with a tight attachment, and the dentin tubule diameter was obviously reduced. Daily brushing with HA and nHA, especially the latter, significantly increased calcium and phosphorus contents on the surface of the dentin dics ( < 0.000). In lead ion adsorption experiment, the lead ion adsorption rate of HA decreased as its concentration increased with the highest adsorption rate of 83.01%; the adsorption rate of nHA increased with its concentration until the adsorption equilibrium was reached, and its highest adsorption rate was 98.79%. A good liner relationship was found between the adsorption ability and concentration of HA.@*CONCLUSIONS@#Compared with HA, nHA has a better capacity for surface mineralization of acid-etched dentin discs and also a better ability of lead ion adsorption.
ABSTRACT
Objective To evaluate the apical sealing ability of iRoot SP root canal sealer in oval-root canal. Methods After root canals were instrumented by Mtwo, 28 premolars with oval-root canal were randomly divided into 2 groups, 14 teeth in each. The root canals were obturated with AH Plus (group A) and iRoot SP (group B) by modified continuous wave condensation technique. The apical leakage was evaluated by dye penetration method and transparent teeth technique. Results Mean depth of leakage was (0.92 ± 0.26) mm for group A and (0.84 ± 0.40) mm for group B. There was no significant difference between the two groups (t=0.506, P > 0.05). Conclusion The apical sealing ability of iRoot SP is equivalent to AH Plus in oval-root canal.
ABSTRACT
Objective To study the capacity of dentifrice containing hydroxyapatite (HA) particles with various grain sizes on the sorption of Cu (Ⅱ) ion from aqueous solution. Methods Three groups of dentifrice suspensions containing 3% HA particles with 60 nm grain size, 3% HA particles with 12 μm grain size, and blank dentifrice were prepared with serial concentrations. Copper ion solutions with initial concentration of 4.0 mg/L were mixed with dentifrice suspensions respectively and then been kept still for 24 hours. The residual copper ion concentration of the supernatant was measured by inductively coupled plasma emission spectrometer and the sorption rate of copper ion was calculated. Results The residual copper ion concentration of the supernatant decreased with increase of the concentration of dentifrice suspensions. The sorption rate of copper ion of dentifrice containing 60 nm HA was highest among the three groups. Conclusion Nano HA should be added into dentifrice to enhance the sorption capacity of copper ion from aqueous solution.